United States & Canada - EN

Heat-Soaking

logo Guardian
What's your challenge?
Design with glass

From anti-reflection to color tints, modern glass enhances design in many ways.

Build with glass

Whatever the construction challenge, we have the glass to help meet it.

Glass for your home

See how the correct choice of glass can help transform a home – and even our wellbeing.

Highlights
7 St. Thomas

Curved glass contributes to harmony between Victorian and contemporary design

Midlands Technical College Library

When glass helps to create a comfortable learning environment

ARO - 242 West 53rd Street

Floor to ceiling windows provide light, transparency and sweeping views of Central Park

All our projects

From landmark construction projects to innovative residential builds, this is how our glass can make the difference

Highlights
Our story

Just as we were in 1932, we're ready to meet the challenges of now and the future

Sustainability

Find out more about how glass can support sustainable design

Quality control

We strive for quality in everything we do

Heat-Soaking

Illustrations for Catalogues

All float glass contains some level of imperfection. One type of imperfection is nickel sulfide (NiS) inclusion. Most NiS inclusions are stable and don’t cause any problems. There is, however, the potential for NiS inclusions that may cause spontaneous breakage in tempered glass without any load or thermal stress being applied.

Heat soaking is a process that may expose NiS inclusions in tempered glass. The process involves placing the tempered glass inside a chamber and raising the temperature to approximately 550°F or 287° to accelerate NiS expansion. This causes glass containing NiS inclusions to break in the heat soak chamber, thus reducing the risk of potential field breakage.

The heat-soaking process is not 100 percent effective, adds cost and carries the risk of reducing the compressive stress in tempered glass.

Guardian offers SunGuard® coated glass products that can be safely heat soaked if it is determined the heat-soaking process is necessary.

Heat-strengthened glass has a much lower potential incidence of spontaneous breakage than tempered glass. For applications where additional glass strength is required due to thermal stress, and safety glass is not mandated, Guardian recommends heat-strengthened or laminated glass to reduce the potential for spontaneous breakage.

Nickel Sulfide (NiS) inclusions:

While extremely rare, nickel sulfide inclusions are another potential cause of breakage.

Nickel sulfide (NiS) inclusions can occur if nickel-rich contaminants are present during the manufacturing process. These contaminants, such as stainless steel, can combine with sulphur to form NiS inclusions.

When glass is heat treated to obtain fully tempered glass, NiS inclusions change size from what is known as a low-temperature (LT) structure to a high-temperature (HT), crystalline structure. When cooled quickly, the NiS particle is unable to change completely back to its original form (LT).

Over a certain period of time, NiS will slowly convert to its (LT) form but with an increase in volume of about 2 to 4 percent. That increase in size can cause breakage. Float glass manufacturers work extremely hard to avoid any nickel-based contaminants in the batch mix. Instances of NiS inclusions are very unusual.

Design professionals can reduce the risk of breakage due to inclusions by specifying heat-strengthened glass, heat-soaking for fully tempered glass or laminated glass.

Float glass

Specifications tools

Find out our easy-to-use, advanced software for glass and glazing specification.

,

Technical Resources Library

Access a wealth of technical notes to enhance your knowledge about glass!

Guardian Glass Training Center
1188191981

Guardian Glass Training Center

Learn the glass fundamentals in a fun and interactive way, at your own pace!